Preparing a magnetically responsive single-wall carbon nanohorn colloid by anchoring magnetite nanoparticles

A single-wall carbon nanohorn (SWNH) colloid was made to be magnetically responsive by anchoring magnetite nanoparticles prepared by the homogeneous mixing of FeCl(2)-FeCl(3) and NaOH solutions. Transmission electron microscopy observation showed the high dispersion of magnetite particles of 2-9 nm on the surface of the SWNH colloid, coinciding with the broad X-ray diffraction peaks of the magnetites. The magnetization measurements showed that the magnetite nanoparticles-anchored SWNH (mag-SWNH) colloid has the hybrid property of ferrimagnetism and superparamagnetism. It was demonstrated that mag-SWNH colloid dispersed in water by sonication responded to an external magnetic field, gathering toward a magnet. N(2) adsorption experiments showed the high nanoporosity of mag-SWNHs and that magnetite nanoparticles were preferably anchored at "nanowindow" sites and the entrance sites of interstitial pores. This magnetically responsive SWNH colloid should contribute to the field of drug delivery.