Shock-induced structural phase transition, plasticity, and brittle cracks in aluminum nitride ceramic

Paulo S Branicio1, Rajiv K Kalia, Aiichiro Nakano

  • 1Collaboratory for Advanced Computing and Simulations, Department of Chemical Engineering and Materials Science, University of Southern California, Los Angeles, California 90089-0242, USA.

Physical Review Letters
|April 12, 2006
PubMed

More Related Videos

Determining the Mechanical Strength of Ultra-Fine-Grained Metals05:04

Determining the Mechanical Strength of Ultra-Fine-Grained Metals

Published on: November 22, 2021

Spark Plasma Sintering Apparatus Used for the Formation of Strontium Titanate Bicrystals11:17

Spark Plasma Sintering Apparatus Used for the Formation of Strontium Titanate Bicrystals

Published on: February 9, 2017

Related Concept Videos

Plasticity00:58

Plasticity

Plasticity is the property where an object loses its elasticity and undergoes irreversible deformation, even after the deformation forces are eliminated. If a material deforms irreversibly without increasing stress or load, then this is called ideal plasticity. For example, when a force is applied to an aluminum rod, it changes its shape, but it does not return to its original shape once the force is removed. Plastic deformation or ductility is thus a permanent deformation or change in the...
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and reloaded.
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
Plastic Deformations01:19

Plastic Deformations

Plastic deformation represents a fundamental concept in materials science, which explains the irreversible change in the shape of a material when it experiences stress beyond its elastic capability. This phenomenon is important in structural engineering, especially in designing and analyzing cantilever beams—structures that are securely fixed at one end and bear loads at the opposite end. When these beams are subjected to loads within their elastic range, they will return to their original...
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...