The high-pressure phase of zincite
Journal of Synchrotron Radiation
|September 1, 1995
Abstract:
Synchrotron-radiation X-ray diffraction studies of ZnO have been performed with special emphasis on the rock-salt-type high-pressure phase. The wurtzite (B4) to rock salt (B1) phase transformation is accompanied by a volume collapse of 18%, which is a very large effect. The lattice constant of the B1 phase at ambient pressure is a(0) = 4.280 (4) A, and the bulk modulus is B(0) = 170 (10) GPa. Comparisons are made with a recently published theoretical equation of state obtained from ab initio perturbed-ion calculations.
Related Concept Videos
01:26EDTA: Auxiliary Complexing Reagents
EDTA titrations are usually carried out in highly basic conditions, where the fully deprotonated form of EDTA, Y4−, actively complexes with the free metal ions in the solution. Several metal ions precipitate as hydrous oxide (hydroxides, oxides, or oxyhydroxides) under these conditions, lowering the concentration of free metal ions in the solution. For this reason, auxiliary complexing agents or ligands such as ammonia, tartrate, citrate, or triethanolamine are used in EDTA titrations to...
00:56Extraction: Advanced Methods
Metal ions can be separated from one another by complexation with organic ligands–the chelating agent– to form uncharged chelates. Here, the chelating agent must contain hydrophobic groups and behave as a weak acid, losing a proton to bind with the metal. Since most organic ligands used in this process are insoluble or undergo oxidation in the aqueous phase, the chelating agent is initially added to the organic phase and extracted into the aqueous phase. The metal-ligand complex is formed in...
03:02Standard Electrode Potentials
On comparing the reactivity of silver and lead, it is observed that the two ionic species, Ag+ (aq) and Pb2+ (aq), show a difference in their redox reactivity towards copper: the silver ion undergoes spontaneous reduction, while the lead ion does not. This relative redox activity can be easily quantified in electrochemical cells by a property called cell potential. This property is commonly known as cell voltage in electrochemistry, and it is a measure of the energy which accompanies the charge...
01:28Transition Zone
The transition zone in concrete is a critical area where aggregate meets cement paste, marked by a distinct porosity and weakness compared to the surrounding material. The adhesion around the aggregates is primarily due to Van Der Waals forces. The voids within this zone influence its robustness; initially, it is less durable than the surrounding bulk mortar due to larger voids. Initially, when concrete is compacted, a higher water-cement ratio near the aggregates leads to the formation of...
02:49Corrosion
The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
01:19Diazonium Group Substitution: –OH and –H
Nitrous acid, a weak acid, is prepared in situ via the reaction of sodium nitrite with a strong acid under cold conditions. This nitrous acid prepared in situ reacts with primary arylamines to form arenediazonium salts. Such reactions are known as diazotization reactions. As shown in Figure 1, the formation of arenediazonium salts begins with the decomposition of nitrous acid in an acidic solution to give nitrosonium ions.