CeO2 nanorods and gold nanocrystals supported on CeO2 nanorods as catalyst

The formation mechanism of uniform CeO2 structure at the nanometer scale via a wet-chemical reaction is of great interest in fundamental study as well as a variety of applications. In this work, large-scale well-crystallized CeO2 nanorods with uniform diameters in the range of 20-30 nm and lengths up to tens of micrometers are first synthesized through a hydrothermal synthetic route in 5 M KOH solution at 180 degrees C for 45 h without any templates and surfactants. The nanorod formation involves dehydration of CeO2 nanoparticles and orientation growth along the 110 direction in KOH solution. Subsequently, gold nanoparticles with crystallite sizes between 10 and 20 nm are loaded on the surface of CeO2 nanorods using HAuCl4 solution as the gold source and NaBH4 solution as a reducing agent. The synthesized Au/CeO2 nanorods demonstrate a higher catalytic activity in CO oxidation than the pure CeO2 nanorods.