Synthesis and electrical transport of single-crystal NH4V3O8 nanobelts

Monoclinic NH(4)V(3)O(8) single-crystalline nanobelts with widths of 80-180 nm, thicknesses of 50-100 nm, and lengths up to tens of micrometers have been synthesized at large scale in an ammonium metavanadate solution by a templates/catalysts-free route. Such nanobelts grow along the direction of [010]. The individual NH(4)V(3)O(8) nanobelt exhibits nonlinear, symmetric current/voltage (I/V) characteristics, with a conductivity of 0.1-1 S/cm at room temperature and a dielectric constant of approximately 130. The dominant conduction mechanism is based on small polaron hopping due to ohmic mechanism at low electric field below 249 V/cm due to Schottky emission at medium electric field between 249 and 600 V/cm and due to the Poole-Frenkel emission mechanism at high field above 600 V/cm.