A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size
Published on: October 17, 2016
Polysaccharide surface engineering of poly(D, L-lactic acid) via electrostatic self-assembly technique and its
1College of Bioengineering, Key Lab of Biomechanics and Tissue Engineering of State Education Ministry, Chong Qing University, Chong Qing, 400044, P R China. kaiyong_cai@cqu.edu.cn
Abstract:
The objective of this study was to surface modify the poly (D, L-lactic acid) (PDLLA) films and assess the effects of the modified surfaces on the functions of osteoblasts cultured in vitro. A layer-by-layer (LBL) self assembly technique, was used leading to the formation of multilayers on the PDLLA film surfaces. Chitosan (Chi) and poly (styrene sulfonate, sodium salt) (PSS) were utilized as polycation and polyanion in this study, respectively. The layer structure was investigated by using X-ray photoelectron spectroscopy (XPS) and water contact angle measurement, respectively. XPS analysis displayed the presence of chitosan on PDLLA surface. A full coverage of coating with PSS/Chi layers was achieved on the PDLLA surface only after the deposition layers of PEI/(PSS/Chi)2. These results showed that PDLLA films could be modified with PSS/Chi pairs which may affect the biocompatibility of the modified PDLLA films. To confirm this hypothesis, cell proliferation, cell viability as well as alkaline phosphtase activity of osteoblasts on layer-by-layer modified PDLLA films as well as control samples were investigated in vitro. The proliferation of osteoblasts on modified PDLLA films was found to be greater than that on control (p < 0.05 and p < 0.01) after 1, 4 and 7 days culture, respectively. Cell viability measurement showed that the PSS/Chi modified PDLLA films have higher cell viability (p < 0.01) than control. Osteoblast differentiation function (ALP) on LBL-modified PDLLA film was found significantly higher (p < 0.01) than that of virgin PDLLA films. These data suggests that PSS/Chi pair was successfully employed to surface modify PDLLA film via a layer-by-layer technique, and enhanced its cell biocompatibility.