Development of diclofenac sodium releasing bio-erodible polymeric nanomats

Application of nanofiber-based nanomats in medicine is attractive and thanks to the 3D nanostructure and the high surface to volume ratio they are excellent for local controlled drug delivery. The use of bioactive bioerodible polymers for developing drug delivery nanomats may allow for drug release and targeting control. Objective of the current study was to evaluate the suitability of bioerodible polymeric material based on n-butyl hemiester of [poly(maleic anhydride-alt-2-methoxyethyl vinyl ether)] (PAM14) for the preparation of nanomats for controlled administration of anti-inflammatory, diclofenac sodium (DS) drug. Samples were prepared using different polymer concentrations (5-10%) in either ethanol or acetic acid as solvent. Morphology was investigated by using scanning electron microscopy (SEM). Thermal analysis such as differential scanning calorimetry (DSC) was performed to detect effect on polymer arrangement. DS localization in electrospun nanomats was evaluated by using electron back scattering microanalysis, based on the detection of chlorine, and drug release kinetics was assessed using UV-Vis. Average fiber diameter resulted in the range of 100 nm to 1.0 microm and a homogeneous distribution of the loaded drug into the fibers was observed. The DS release was immediate and despite the preliminary nature of the performed electrospinning experiments, the achieved results appear promising for the future development of a novel system for the controlled and targeted administration of drug and active agent.