Preparation and characterization of aligned carbon nanotube-ruthenium oxide nanocomposites for supercapacitors

A novel type of ruthenium oxide (RuO(2))-modified multi-walled carbon nanotube (MWNT) nanocomposite electrode (RuO(2)/MWNT) for supercapacitors has been prepared. The nanocomposites were formed by depositing Ru by magnetic-sputtering in an Ar/O(2) atmosphere onto MWNTs, which were synthesized on Ta plates by chemical vapor deposition. Cyclic voltammetry, chronopotentiometry, and electrochemical impedance measurements were applied to investigate the performance of the RuO(2)/MWNT nanocomposite electrodes. The capacitance of the MWNT electrodes in 1.0 M H(2)SO(4) is significantly increased from 0.35 to 16.94 mF cm(-2) by modification with RuO(2). The RuO(2) film on the surface of the nanotubes is composed of small crystal grains with tilted bundle-like microstructures, as observed by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The results demonstrate a promising route to prepare RuO(2)/MWNT-based double-layer supercapacitors.