Related Experiment Video

Updated: Jul 10, 2026

Assembly and Characterization of Polyelectrolyte Complex Micelles
08:44

Assembly and Characterization of Polyelectrolyte Complex Micelles

Published on: March 2, 2020

Microcanonical analysis of association of hydrophobic segments in a heteropolymer

Tao Chen1, Xiangsong Lin, Yuan Liu

  • 1Department of Polymer Science and Engineering, University of Science and Technology of China, Hefei, Anhui, 230026, People's Republic of China.

Physical Review. E, Statistical, Nonlinear, and Soft Matter Physics
|November 13, 2007
PubMed

More Related Videos

MALDI-ToF MS Method for the Characterization of Synthetic Polymers with Varying Dispersity and End Groups06:16

MALDI-ToF MS Method for the Characterization of Synthetic Polymers with Varying Dispersity and End Groups

Published on: October 3, 2025

Anionic Polymerization of an Amphiphilic Copolymer for Preparation of Block Copolymer Micelles Stabilized by π-π Stacking Interactions10:53

Anionic Polymerization of an Amphiphilic Copolymer for Preparation of Block Copolymer Micelles Stabilized by π-π Stacking Interactions

Published on: October 10, 2016

Related Concept Videos

Characteristics and Nomenclature of Homopolymers01:00

Characteristics and Nomenclature of Homopolymers

Polymers that are made up of identical monomer units are called homopolymers. Only one repeating unit is involved in the construction of the homopolymer structure. For example, as depicted in Figure 1, polypropylene is a homopolymer constituted of propylene monomers. Here, the only repeating unit in the polymer chain is propylene.
Radical Chain-Growth Polymerization: Chain Branching01:17

Radical Chain-Growth Polymerization: Chain Branching

The skeletal structure of polymers synthesized via radical polymerization is always branched. For example, the polymerization of ethylene by radical polymerization results in a low-density grade of polyethylene with a heavily branched skeletal structure. Here, the radical site abstracts hydrogen from the growing chain, and the radical site shifts from the end (a primary carbon center) to anywhere within the growing chain (a secondary carbon center). Consequently, the part of the chain from the...
Characteristics and Nomenclature of Copolymers01:24

Characteristics and Nomenclature of Copolymers

Copolymers are the products obtained from the polymerization of multiple monomer species. So, in a polymer chain itself, there can be multiple repeating units that come from different monomers. The process of synthesizing a polymer from different monomer species is called copolymerization. When two monomers are involved, the polymer is known as a bipolymer. Polymers with three and four monomers are termed terpolymers and quaterpolymers, respectively. Figure 1 depicts the copolymerization of...
Determination of Molar Masses of Polymers II01:27

Determination of Molar Masses of Polymers II

Polymer samples typically consist of macromolecular chains with a distribution of lengths, resulting in a range of molar masses rather than a single discrete value. Conventional descriptors such as the number-average molar mass and weight-average molar mass quantify this distribution but do not fully capture polymer behavior in solution..The viscosity-average molar mass provides a more realistic description of polymer behavior in solution because it accounts for the enhanced contribution of...
Determination of Molar Masses of Polymers I01:24

Determination of Molar Masses of Polymers I

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.