Chemical solubility and flexural strength of zirconia-based ceramics
John Chai1, Frederick C S Chu, Tak W Chow
1Northwestern University, Evanston, Illinois, USA.
Purpose:
This study was undertaken to investigate the chemical solubility and flexural strengths of 3 zirconia-based dental ceramics: In-Ceram Zirconia (IZ), In-Ceram 2000 YZ CUBES (YZ Zirconia) (Vita Zahnfabrik), and Cercon (Dentsply). A pressable lithium disilicate-reinforced glass ceramic (IPS Empress 2, Ivoclar Vivadent) was used as a control.
Materials And Methods:
Ten block specimens (12 x 6 x 4 mm) of each ceramic material were prepared for chemical solubility testing. Each specimen was refluxed in 4% acetic acid solution for 16 hours. The percentage loss of mass and the loss of mass per unit of surface area for each specimen were calculated. Ten bar-shaped (21 x 5 x 2 mm) and 10 disk-shaped (16 mm diameter, 1.2 mm thickness) specimens of each ceramic material were prepared and tested for uniaxial flexural strength (UFS) and biaxial flexural strength (BFS). X-ray diffraction analyses were conducted to determine the relative amount of the monoclinic phase of the as-sintered and fractured surfaces of the zirconia ceramics.
Results:
There were no significant differences among the ceramics in chemical solubility by percentage mass or mass/surface area. For UFS, YZ Zirconia (899 +/- 109 MPa) > Cercon (458 +/- 95 MPa) IZ (409 +/- 60 MPa) > Empress 2 (252 +/- 36 MPa). For BFS, YZ Zirconia (1,107 +/- 116 MPa) > Cercon (927 +/- 146 MPa) > IZ (523 +/- 51 MPa) > Empress 2 (359 +/- 43 MPa). The fractured YZ Zirconia surface contained approximately 5 times as much monoclinic phase compared to that of its intact surface. The fractured IZ and Cercon surfaces contained approximately twice as much monoclinic phase compared to those of intact surfaces.
Conclusion:
The ceramics tested all satisfied the chemical solubility allowance required of core ceramic material (type I, Class 1 or type II, Class 1) according to the International Organization for Standardization 6872:1995(E) specifications on dental ceramic. The zirconia-based ceramics possessed significantly higher flexural strengths than the control lithium disilicate ceramic. Their clinical application appears sufficiently promising for long-term clinical studies to be undertaken.
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
02:54Molecular and Ionic Solids
Molecular Solids
Molecular crystalline solids, such as ice, sucrose (table sugar), and iodine, are solids that are composed of neutral molecules as their constituent units. These molecules are held together by weak intermolecular forces such as London dispersion forces, dipole-dipole interactions, or hydrogen bonds, which...
02:19Physical Properties Affecting Solubility
As for any solution, the solubility of a gas in a liquid is affected by the attractive intermolecular forces between solute and solvent species. Unlike solid and liquid solutes, however, there is no solute-solute intermolecular attraction to overcome when a gaseous solute dissolves in a liquid solvent since the atoms or molecules comprising a gas are far separated and experience negligible interactions. Consequently, solute-solvent interactions are the sole...
02:55Solubility of Ionic Compounds
01:12Bonding and Strength of Aggregate
01:21Pozzolans
Fly ash is a...