Carbodiimide cross-linked hyaluronic acid hydrogels as cell sheet delivery vehicles: characterization and interaction...

It was reported that cell-adhesive gelatin discs have been successfully used as delivery vehicles for intraocular grafting of bioengineered corneal endothelial cell sheets. Development of alternative biomaterials to bovine-based gelatin vehicles can potentially eliminate the risk of bovine spongiform encephalopathy. In the present work, to investigate whether it was appropriate for use as cell sheet delivery vehicles, 1-ethyl-3-(3-dimethyl aminopropyl) carbodiimide (EDC) cross-linked hyaluronic acid (HA) hydrogels were studied by determinations of morphological characteristic, mechanical and thermal property, water content, in vitro degradability and cytocompatibility. Glutaraldehyde (GTA) cross-linked HA samples were used for comparison. It was found that HA discs after cross-linking significantly increased its tensile stress but reduced its tensile strain, water uptake and enzymatic degradability. The results of differential scanning calorimetry demonstrated that cross-linking could lead to the alteration of polymer structure. In addition, the EDC-cross-linked HA discs had a smoother surface structure, a faster degradation rate and a relatively lower cytotoxicity as compared to the GTA cross-linked counterparts. It is concluded that EDC can be successfully applied for HA cross-linking to fabricate structurally stable, mechanically reinforced, readily deformable, transparent and cytocompatible HA hydrogel discs with the potential to be applied as delivery vehicles for corneal endothelial cell therapy.