Microhardness and fluoride release of restorative materials in different storage media

This study evaluated the surface microhardness and fluoride release of 5 restorative materials - Ketac-Fil Plus, Vitremer, Fuji II LC, Freedom and Fluorofil - in two storage media: distilled/deionized water and a pH-cycling (pH 4.6). Twelve specimens of each material, were fabricated and the initial surface microhardness (ISM) was determined in a Shimadzu HMV-2000 microhardness tester (static load Knoop). The specimens were submitted to 6- or 18-h cycles in the tested media. The solutions were refreshed at the end of each cycle. All solutions were stored for further analysis. After 15-day storage, the final surface microhardness (FSM) and fluoride release were measured. Fluoride dose was measured with a fluoride-specific electrode (Orion 9609-BN) and digital ion analyzer (Orion 720 A). The variables ISM, FSM and fluoride release were analyzed statistically by analysis of variance and Tukey's test (p<0.05). There was significant difference in FSM between the storage media for Vitremer (pH 4.6 = 40.2 +/- 1.5; water = 42.6 +/- 1.4), Ketac-Fil Plus (pH 4.6 = 73.4 +/- 2.7; water = 58.2 +/- 1.3) and Fluorofil (pH 4.6 = 44.3 +/- 1.8; water = 38.4 +/- 1.0). Ketac-Fil Plus (9.9 +/- 18.0) and Fluorofil (4.4 +/- 1.3) presented higher fluoride release in water, whereas Vitremer (7.4 +/- 7.1), Fuji II LC (5.7 +/- 4.7) and Freedom (2.1 +/- 1.7) had higher fluoride release at pH 4.6. Microhardness and fluoride release of the tested restorative materials varied according to the storage medium.