Flexural strength of veneering ceramics for zirconia

J Fischer1, B Stawarczyk, C H F Hämmerle

  • 1Clinic for Fixed and Removable Prosthodontics, Center for Dental and Oral Medicine, University of Zurich, Plattenstrasse 11, CH-8032 Zurich, Switzerland. jens.fischer@zzmk.uzh.ch

Journal of Dentistry
|March 15, 2008
PubMed
Abstract

Keywords:
flexural strength testingdental ceramicszirconia restorationsceramic material comparison

More Related Videos

Fused Filament Fabrication (FFF) of Metal-Ceramic Components08:43

Fused Filament Fabrication (FFF) of Metal-Ceramic Components

Published on: January 11, 2019

Related Concept Videos

Veneer01:19

Veneer

Veneer refers to a thin sheet of wood, typically produced to a thickness of about one-eighth of an inch or less. This material is crafted through various methods, the most common being rotary cutting. In this process, a log is mounted into a large lathe and spun against a knife edge, peeling off a continuous strip of wood as the knife penetrates deeper into the rotating log, creating a rotary-cut veneer.
Other veneering techniques include plain-slicing, quarter-slicing, and rift-slicing. These...
Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
Design of Prismatic Beams for Bending01:23

Design of Prismatic Beams for Bending

The design of prismatic beams, structural elements with a uniform cross-section, focuses on ensuring safety and structural integrity under load. The design process begins by determining the allowable stress, either from material properties tables, or by dividing the material's ultimate strength by a safety factor. This safety factor is essential for accommodating uncertainties, and varies depending on the material—timber, steel, or concrete—with each having unique strength and stress...
Residual Stresses in Bending01:18

Residual Stresses in Bending

In the study of elastoplastic members subjected to bending moments, understanding the loading and unloading phases is crucial for assessing material behavior and structural integrity. During the loading phase, as the bending moment increases, the material initially responds elastically, adhering to Hooke's Law, where stress is directly proportional to strain. When the load exceeds the yield strength, plastic deformation occurs, resulting in permanent strain and deformation that remains even...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Fiber Reinforced Concrete01:22

Fiber Reinforced Concrete

Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...