Stick slip contact mechanics between dissimilar materials: effect of charging and large friction

Measurements of the contact radius as a function of applied force between a mica surface and a silica surface (mica/silica) in air are reported. The load/unload results show that the contact radius generally increases with applied force. Because of the presence of charging due to contact electrification, both a short-range van der Waals adhesion force and longer-range electrostatic adhesive interaction contribute to the measured force. The results indicate that approximately 20% of the pull-off force is due to van der Waals forces. The contact radius versus applied force results can be fit to Johnson-Kendall-Roberts (JKR) theory by considering that only the short-range van der Waals forces contribute to the work of adhesion and subtracting a constant longer-range electrostatic force. Also, an additional and unexpected step function is superimposed on the contact radius versus applied force curve. Thus, the contact diameter increases in a stepped dependence with increasing force. The stepped contact behavior is seen only for increasing force and is not observed when symmetric mica/mica or silica/silica contacts are measured. In humid conditions, the contact diameter of the mica/silica contact increases monotonically with applied force. Friction forces between the surfaces are also measured and the shear stress of a mica/silica interface is 100 times greater than the shear stress of a mica/mica interface. This large shear stress retards the increase in contact area as the force is increased and leads to the observed stepped contact mechanics behavior.