The effect of sodium-ion implantation on the properties of titanium

This paper deals with the surface modification of titanium by sodium-ion implantation and with the effect of this modification on structure, corrosion resistance, bioactivity and cytocompatibility. The Na ions were implanted with doses of 1 x 10(17) and 4 x 10(17) ions/cm(2) at an energy of 25 keV. The chemical composition of the surface layers formed during the implantation was examined by secondary-ion mass spectrometry (SIMS) and X-ray photoelectron spectroscopy (XPS), and their microstructure--by transmission electron microscopy (TEM). The corrosion resistance was determined by electrochemical methods in a simulated body fluid (SBF) at a temperature of 37 degrees C, after exposure in SBF for various times. The surfaces of the samples were examined by optical microscopy, by scanning electron microscopy (SEM-EDS), and by atomic force microscopy (AFM). Biocompatibility of the modified surface was evaluated in vitro in a culture of the MG-63 cell line and human osteoblast cells. The TEM results indicate that the surface layers formed during the implantation of Na-ions are amorphous. The results of the electrochemical examinations obtained for the Na-implanted titanium samples indicate that the implantation increases corrosion resistance. Sodium-ion implantation improves bioactivity and does not reduce biocompatibility.