A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size
Published on: October 17, 2016
Comparison of morphology and mechanical properties of PLGA bioscaffolds
1Department of Mechanical and Industrial Engineering, University of Toronto, 5 King's College Road, Toronto, Ontario, M5S 3G8, Canada.
Abstract:
In this study, bioscaffolds using poly(DL-lactide-co-glycolide) acid (PLGA) were fabricated and studied. The gas foaming/salt leaching technique in a batch foaming setup was employed, and the effects of material composition of PLGA on the morphology and mechanical properties using this process were investigated. Two material compositions of PLGA 50/50 and 85/15 were used, and characterization of scaffolds fabricated with these materials showed that a lower relative density can be achieved with an increasing poly(DL-lactide) acid (PDLLA) content; however, higher open-cell porosity was obtained with lower PDLLA content. Furthermore, the effect of PLGA composition on modulus of the scaffolds was minor.