Rapid synthesis and characterization of maghemite nanoparticles

Fe2O3-SiO2 nanocomposites were prepared by a sol-gel method using various evaporation surface to volume (S/V) ratios ranging from 0.03 to 0.2. The Fe2O3-SiO2 sols were gelated at various temperatures ranging from 50 degrees C to 70 degrees C, and subsequently they were calcined in air at 400 degrees C for 4 hours. The structure and the magnetic properties of the prepared Fe203-SiO2 nanocomposites were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), differential thermal analysis (DTA), and vibrating sample magnetometer (VSM) measurements. The gelation temperature of the Fe2O3-SiO2 sols influenced strongly the particle size and crystallinity of the maghemite nanoparticles. It was observed that the particle size of maghemite nanoparticles increased with the increasing of the gelation temperature of the sols, which may be due to the agglomeration of the maghemite particles at elevated temperatures inside the microporosity of the silica matrix during the gelation process, and the subsequent calcination of these gels at 400 degrees C resulted in the formation of large size iron oxide particles. Magnetization studies at temperatures of 10, 195, and 300 K showed superparamagnetic behavior for all the nanocomposites prepared using the evaporation surface to volume ratio (S/V) of 0.1, 0.2, 0.09, and 0.08. The saturation magnetization, Ms, values measured at 10 K were 5.5, 8.5, and 9.5 emu/g, for the samples gelated at 50, 60, and 70 degrees C, respectively. At the gelation temperature of 70 degrees C, gamma-Fe2O3 crystalline superparamagnetic nanoparticles with the particle size of 9 +/- 2 nm were formed in 12 hours for the samples prepared at the S/V ratio of 0.2.