Fabrication of lead-free piezoelectric (Na(0.5)K(0.5))NbO(3) ceramics by a modified solid-state reaction method

Sodium potassium niobate, (Na(0.5)K(0.5))NbO(3), fine powder has been successfully synthesized at the low temperature of 550 degrees C through a modified solid-state reaction method, in which urea [CO(NH(2))(2)] plays an important role. High-density (Na(0.5)K(0.5))NbO(3) ceramics could be obtained by conventional sintering of the synthesized (Na(0.5)K(0.5))NbO(3) fine powder with the addition of 0.03 mol% Co(3)O(4) as a sintering additive. The crystal structure, microstructure, and dielectric and piezoelectric properties were characterized. The (Na(0.5)K(0.5))NbO(3) ceramic showed a comparatively saturated P-E hysteresis loop. The (Na(0.5)K(0.5))NbO(3) ceramic also displayed piezoelectricity with a piezoelectric constant d(33) of 126 pC/N and a planar electromechanical coupling factor k(p) of 33%.