Contact fracture of full-ceramic crowns subjected to occlusal loads

Dongsheng Zhang1, Chenglin Lu, Xiuyin Zhang

  • 1Department of Mechanics, Shanghai University, 99 Shangda Road, Shanghai 200444, PR China. donzhang@staff.shu.edu.cn

Journal of Biomechanics
|September 12, 2008
PubMed

More Related Videos

Imaging of the Microstructural Failure Mechanism in the Human Hip08:43

Imaging of the Microstructural Failure Mechanism in the Human Hip

Published on: September 29, 2023

Related Concept Videos

General Case of Eccentric Axial Loading01:12

General Case of Eccentric Axial Loading

Unsymmetrical bending occurs when the bending moment applied to a structural member does not align with its principal axis. This misalignment leads to complex stress distributions and deflection patterns that differ from symmetrical bending, which are essential for designing structures to withstand different loading conditions.
Consider a member subjected to equal and opposite forces that are applied along a line that does not coincide with the member's neutral axis. In unsymmetrical bending,...
Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
Stresses under Combined Loadings01:23

Stresses under Combined Loadings

When analyzing a bent tube with a circular cross-section subjected to multiple forces, it is crucial to determine the stress distribution in order to maintain structural integrity under varied load conditions.
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...
Normal Strain under Axial Loading01:20

Normal Strain under Axial Loading

Normal strain under axial loading is an important concept in the field of mechanics of materials. Axial loading implies the application of a force along the axis of a material, like a column or bar. This force can either compress or stretch the material. In the context of axial loading, normal strain is the deformation experienced by the material in the direction of the loading force. It's calculated as the change in length divided by the original length of the material. This unitless ratio...
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...