Cementless Gustilo-Kyle and BIAS total hip arthroplasty: 2- to 5-year results

We conducted extensive radiographic and clinical examination of 58 cementless total hip arthroplasties. Forty BIAS femoral stems had heads made of Co-base F 75 alloy and 18 Gustilo-Kyle femoral stems had Ti6A14V alloy heads. The cross-sectional geometry and location of the porous coating pads of the two stem types was identical, the BIAS component being slightly shorter. At the last follow-up, 27.8% of the Gustilo-Kyle femoral components and 2.5% of the BIAS femoral components were unstable. None of the acetabular components in the BIAS group as against 38.9% of the acetabular components in the Gustilo-Kyle group demonstrated wear of more than 1 mm. All unstable components which did not suffer intraoperative fracture had also acetabular wear of more than 1 mm. The only case with endosteal erosion was seen in a patient with an unstable implant displaying the most extensive wear. Nonparametric statistical analysis showed that the patients with Ti6A14V/polyethylene bearing surfaces had a statistically significantly higher extent of wear and a statistically significant higher incidence of femoral component loosening than patients with CrCoMo/polyethylene bearing surfaces.