Expression of Cementitious Pore Solution and the Analysis of Its Chemical Composition and Resistivity Using X-ray Fluorescence
06:27

Expression of Cementitious Pore Solution and the Analysis of Its Chemical Composition and Resistivity Using X-ray Fluorescence

Published on: September 23, 2018

Analysis of cement by atomic absorption spectrophotometry and volumetric method

K K Choi1, L Lam, S F Luk

  • 1Laboratory, China Cement Co. (HK) Ltd., Tap Shek Kok, Tuen Mun, Hong Kong.

Talanta
|January 1, 1994
PubMed

More Related Videos

Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way07:42

Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way

Published on: November 21, 2017

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent11:14

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

Published on: February 21, 2017

Related Concept Videos

Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Fineness of Cement01:15

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
Measurement of Air Content in Concrete01:23

Measurement of Air Content in Concrete

Air content measurement in concrete is critical for ensuring structural integrity and durability of concrete structures, especially in environments prone to severe weather conditions. Accurate air content analysis optimizes concrete's resistance to freeze-thaw cycles and enhances its workability and strength. Several methods are standardized under ASTM guidelines to measure the air content in fresh concrete, each suitable for different concrete types and conditions.
The pressure method,...
Atomic Absorption Spectroscopy: Lab01:21

Atomic Absorption Spectroscopy: Lab

For AAS measurements, samples must be introduced as clear solutions, often requiring extensive preliminary treatment to dissolve materials like soils, animal tissues, and minerals. Common methods for sample preparation include treatment with hot mineral acids, wet ashing, combustion in closed containers, high-temperature ashing, or fusion with reagents.
 Solutions containing organic solvents, such as low-molecular-mass alcohols, esters, or ketones, enhance absorbances by increasing nebulizer...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Volatilization01:10

Volatilization

Volatilization gravimetry is an analytical technique that measures the mass lost due to the volatilization of the substance. This technique is used to estimate the amount of volatile material in a sample. To perform this method, heat a known amount of the sample to a high temperature in a crucible or other suitable vessel. The volatile substance in the sample evaporates, and the vapor is completely expelled from the crucible either by heating the sample or bubbling a stream of inert gas through...