Magnetotransport and structural properties of nanocrystalline FeAgAl thin films
1Department of Physics, Indian Institute of Technology Bombay, Mumbai 400076, India.
Abstract:
Structural and magnetotransport properties of metallic Fe(x)Ag(y)Al(z) nanogranular thin films were studied. These films with several compositions were prepared by dc magnetron sputtering. X-ray diffraction (XRD) measurements carried out on the samples show only Ag(111) peaks. The d-spacings determined from the Ag(111) peaks are smaller than the standard value for bulk Ag indicating a partial substitution of Fe and Al atoms in Ag matrix. Transmission electron diffraction (TEM) patterns show a number of Ag rings. Both XRD and TEM studies did not reveal any diffraction peaks due to Fe or Al. The average particle size determined from the TEM micrograph is 5.9 nm. This value is in good agreement with the grain size determined from the XRD patterns for the Al substituted samples. The MR was found to increase for smaller Al concentration and it decreases with further increase in Al content. In the samples investigated magnetoresistance ratio reaches a maximum value of about 4.5% for the Fe27Ag63Al10 film.
Related Concept Videos
01:31Ferromagnetism
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.