Effects of the Ar ions pre-amorphization of Si substrate on interface mixing of Fe/Si bilayers

Ion beam mixing of Fe/Si bilayers, induced by 100 keV (40)Ar ions at room temperature was investigated. Rutherford backscattering spectroscopy (RBS), atomic force microscopy (AFM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were applied for structural characterization. The main focus of this study was on the influence of the substrate structure on interface mixing. The influence of the substrate structure is due to the two classes of irradiated bilayers, Fe thin films deposited on crystalline or pre-amorphized Si substrates. An about 76% higher efficiency of atomic transport across the pre-amorphized Fe/a-Si interface as compared to that of Fe/c-Si bilayers was observed.