Activated carbons prepared from wood particleboard wastes: characterisation and phenol adsorption capacities

The problems of valorisation of particleboard wastes on one hand, and contamination of aqueous effluents by phenolic compounds on the other hand, are simultaneously considered in this work. Preparation of activated carbons from a two steps thermo-chemical process, formerly designed for generating combustible gases, is suggested. The resultant carbonaceous residue is activated with steam at 800 degrees C. Depending on the preparation conditions, surface areas within the range 800-1300 m(2)/g are obtained, close to that of a commercial activated carbon (CAC) specially designed for water treatment and used as a reference material. The present work shows that particleboard waste-derived activated carbons (WAC) are efficient adsorbents for the removal of phenol from aqueous solutions, with maximum measured capacities close to 500 mg/g. However, most of times, the adsorption capacities are slightly lower than that of the commercial material in the same conditions, i.e., at equilibrium phenol concentrations below 300 ppm. Given the extremely low cost of activated carbons prepared from particleboard waste, it should not be a problem to use it in somewhat higher amounts than what is required with a more expensive commercial material. Phenol adsorption isotherms at 298 K were correctly fitted by various equations modelling type I and type II isotherms for CAC and WAC, respectively. Phenol adsorption isotherms of type II were justified by a 3-stages adsorption mechanism.