Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization
09:02

Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization

Published on: July 9, 2015

Controlled step growth of molecularly linked gold nanoparticles: from metallic monomers to dimers to polymeric

Irshad Hussain1, Mathias Brust, Justas Barauskas

  • 1Centre for Nanoscale Science, Department of Chemistry, University of Liverpool, UK. ihussain@lums.edu.pk

Langmuir : the ACS Journal of Surfaces and Colloids
|January 23, 2009
PubMed

More Related Videos

A Simple Method for the Size Controlled Synthesis of Stable Oligomeric Clusters of Gold Nanoparticles under Ambient Conditions08:21

A Simple Method for the Size Controlled Synthesis of Stable Oligomeric Clusters of Gold Nanoparticles under Ambient Conditions

Published on: February 5, 2016

Gold Nanoparticle Synthesis13:42

Gold Nanoparticle Synthesis

Published on: July 10, 2021

Related Concept Videos

Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
Radical Chain-Growth Polymerization: Overview01:10

Radical Chain-Growth Polymerization: Overview

Chain-growth or addition polymerization is successive addition reactions of monomers with a polymer chain. In radical chain-growth polymerization, the reaction proceeds via a free-radical intermediate. The free radical is formed from radical initiators, which spontaneously generate free radicals by homolytic fission. Organic peroxides (such as dibenzoyl peroxide, as shown in Figure 1) or azo compounds are popular radical initiators. A low concentration ratio of radical initiator to monomer is...
Cationic Chain-Growth Polymerization: Mechanism00:57

Cationic Chain-Growth Polymerization: Mechanism

The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the generated carbocation,...
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta catalyst, high molecular...
Anionic Chain-Growth Polymerization: Mechanism01:04

Anionic Chain-Growth Polymerization: Mechanism

The mechanism for anionic chain-growth polymerization involves initiation, propagation, and termination steps. In the initiation step, a nucleophilic anion, such as butyl lithium, initiates the polymerization process by attacking the π bond of the vinylic monomer. As a result, a carbanion, stabilized by the electron‐withdrawing group, is generated. The resulting carbanion acts as a Michael donor in the propagation step and attacks the second vinylic monomer, which acts as a Michael acceptor.