Adsorption behavior and mechanism of arsenate at Fe-Mn binary oxide/water interface

Preliminary study revealed that a prepared Fe-Mn binary oxide adsorbent with a Fe:Mn molar ratio of 3:1 was more effective for As(V) removal than pure amorphous FeOOH, which was unanticipated. In this paper, the As(V) adsorption capacities of Fe-Mn binary oxide and amorphous FeOOH were compared in detail. Furthermore, the adsorption behaviors as well as adsorption mechanism of As(V) at the Fe-Mn binary oxide/water interface were investigated. The higher uptake of As(V) by the Fe-Mn binary oxide may be due to its higher surface area (265 m(2)/g) and pore volume (0.47 cm(3)/g) than those of amorphous FeOOH. The As(V) adsorption process on the Fe-Mn binary oxide is endothermic and the increase of temperature is favoring its adsorption. A slight increase in the As(V) adsorption was observed with increasing ionic strength of the solution, which indicated that As(V) anions might form inner-sphere surface complexes at the oxide/water interface. The Zeta potential along with FTIR analysis confirmed further the formation of inner-sphere surface complexes between As(V) anions and the surface of Fe-Mn binary oxide. In addition, the influences of coexisting ions such as phosphate, bicarbonate, silicate, sulfate, chloride, calcium and magnesium which are generally present in groundwater on As(V) adsorption were examined. Among the tested anions, chloride and sulfate had no significant effect on As(V) removal, silicate decreased obviously the As(V) removal, while phosphate caused the greatest percentage decrease in As(V) adsorption. On the contrary, the presence of cations of Ca(2+) and Mg(2+) enhanced the adsorption of As(V).