How do porosity-inducing techniques affect antibiotic elution from bone cement? An in vitro comparison between...

Increasing the porosity of an antibiotic-loaded cement spacer increases the antibiotic elution, but the correlation between porosity and antibiotic elution is not well documented. The purposes of this study was to attempt new porosity-increasing methods and to investigate the correlation between antibiotic elution and both total and surface porosity.

Five types of antibiotic-loaded bone cement (ALBC) using 2 g cefazolin and 40 g cement were prepared. Other than manual mixing, hydrogen peroxide was used as a foaming agent and a mixing drill piece was used as a mechanical device to try to induce porosity when mixing the cement. Elution of antibiotic into phosphate-buffered saline was measured from 1 h to 1 week. Surface porosity was calculated from density values which were measured with a density kit and an electronic balance, while total porosity was quantified using micro-computed tomography.

When a mixing drill piece was used to induce porosity, we observed a significant increasin antibiotic elution compared to a manually mixed ALBC. On the other hand, hydrogen peroxide reduced the elution significantly. Mild correlation between the total amount of cluted in 1 week antibiotic elution and total porosity was observed.

In terms of improving elution, the mixing drill piece seemed to be efficient. A relationship between surface porosity and elution efficacy was not observed.