Analysis of temperature-promoted and solvent-assisted cross-linking in sulfonated poly(ether ether ketone) (SPEEK)
M Luisa Di Vona1, Emanuela Sgreccia, Silvia Licoccia
1Dipartimento di Scienze e Tecnologie Chimiche, Università di Roma Tor Vergata, Roma, Italy. divona@uniroma2.it
Abstract:
Sulfonated poly(ether ether ketone) (SPEEK) membranes were thermally treated at temperatures between 120 and 160 degrees C. Water uptake measured at different relative humidity values or by full immersion in water between 25 and 145 degrees C was found to depend very strongly on previous thermal treatment and casting solvent. Water-uptake coefficient values as low as 10-15 even upon immersion in water at 100 degrees C were obtained with membranes treated at 160 degrees C. This effect is related to cross-linking by SO2 bridges between macromolecular chains. An important role is also played by the casting solvent: among the investigated solvents, dimethylsulfoxide (DMSO) gave the best results. A chemical kinetics model is outlined that permits the estimation of the relevant kinetic parameters, especially the activation energy of the cross-linking reaction, which was found to be about 60 kJ/mol. These results are of significant importance for the improvement of proton-exchange membrane fuel cells.