Robust gold-decorated silica-titania pebbles for low-temperature CO catalytic oxidation

A deposition-precipitation (DP) process was used to prepare silica-titania core-shell pebbles decorated with nanocrystalline gold suitable for low-temperature catalytic oxidation of carbon monoxide (CO). The microstructure, phase content, crystallography, and catalytic activity were correlated with the pH (3-8), aging time (15, 30, 60 min), and heat treatment employed for gold crystallization (200-400 degrees C). A homogeneous metal distribution, high gold loading (3.7-4.4 wt %), and superior interfacial adhesion between gold and titania were obtained when the support pebbles were prepared at 600 degrees C, a temperature lower than that required for the anatase-to-rutile transformation. Nucleation and growth of {111} faceted gold was favored at mid-pH (6.4-8), while smaller crystals (<7.5 nm) were obtained at short aging times (