The formation of vertically aligned biaxial tungsten nanorods using a novel shadowing growth technique

Biaxially textured tungsten nanorods (A15 crystal structure) have been grown by oblique angle DC magnetron sputtering using a novel rotation mode called 'two-step rotation'. In this mode, the substrate is given a fast rotation through 180 degrees at 90 rpm and this is followed by a rest period of 30 s. These nanorods are vertically aligned and have a [100] texture normal to the substrate along with preferential in-plane texture as shown by x-ray pole figure analysis. In contrast, the tungsten nanorods obtained without substrate rotation are slanted at an angle of approximately 45 degrees and have a [100] texture tilted 16 degrees with respect to the substrate normal. The flux is incident from two diametrically opposite points on the sample at an oblique angle, averaging out the growth into vertical columns that retain the in-plane texture. Scanning electron microscopy shows that the tungsten nanorods have a mixture of {211} and {421} crystal habits; these planes are both minimum surface energy planes for a cubic A15 crystal structure.