Fabrication of alpha-Fe2O3 nanopowder modified glassy carbon electrode for applications in electrochemical sensing

In the present study, Fe2O3 nanopowder has been grown by Ultrasonic mist chemical vapor deposition (UM-CVD), which is a promising method for large area deposition at low temperatures taking in to account of its simplicity, inexpensiveness and safety. Room temperature XRD results revealed prominent hematite phase with intense (104) reflection and was also in agreement with the HR-TEM results. In situ high temperature X-ray diffraction (XRD) studies clearly indicated the change of phase from hematite to magnetite as the temperature increases above 300 degrees C. The surface morphology and particle size distribution of Fe2O3 nanopowder were characterized using field emission scanning electron microscope (FE-SEM) and high resolution transmission electron microscope (HR-TEM), which revealed that the particles were spherical in nature and distributed in range of 50-100 nm. SQUID magnetometry results indicate the ferromagnetic nature of the nanopowder with crystallite size of 6 nm as calculated from M-H curve. Transmittance of approximately 55% and estimated direct band gap of 2.5 eV was observed. Further, the nanopowder was used to modify glassy carbon electrode (GCE) and the modified electrode was found to exhibit electrocatalytic activity for the oxidation of dopamine. It is expected that the nanopowder will exhibit promising applications in the development of sensors.