Synthesis and characterization of poly(vinyl alcohol) membranes with quaternary ammonium groups for wound dressing

2-[(acryloyloxy)ethyl]Trimethylammonium chloride (AETMAC) was grafted onto poly(vinyl alcohol) (PVA) using ceric ammonium nitrate (CAN) as a redox initiator. A series of graft co-polymer (PVA-g-PAETMAC) membranes with different contents of AETMAC were prepared with a casting method. The incorporation of AETMAC into PVA chains was confirmed by element analysis and Fourier transform infrared spectroscopy. The effects of grafting on the thermal properties, water take, water vapor transmission rate (WVTR), contact angle, antibacterial activity and cytotoxicity of PVA-g-PAETMAC membranes were investigated. The experiment results showed that PVA-g-PAETMAC membrane has a higher equilibrium swelling ratio, surface hydrophilicity and WVTR than pure PVA membrane. Moreover, the higher the content of AETMAC, the higher were equilibrium swelling ratio, surface hydrophilicity and WVTR. In vitro bacterial adhesion study demonstrated a significantly reduced number of Staphylococcus aureus and Escherichia coli on PVA-g-PAETMAC surfaces when compared to PVA surface. In addition, no significant difference in the in vitro cytotoxicity was observed between PVA and PVA-g-PAETMAC membranes. The presence of quaternary ammonium groups did not reduce L929 cell growth. Therefore, the PVA-g-PAETMAC membranes have the potential for wound-dressing application.