Reversible switching between hydrophilic and hydrophobic superparamagnetic iron oxide microspheres via one-step...

We describe the use of hydrophobic poly(aryl ether) dendrons to peripherally functionalize hydrophilic amine-containing superparamagnetic iron oxide microspheres (SPIO-NH2) in one step via imine formation. The reversible formation of imine bonds in the absence/presence of water renders dynamic control of the hydrophilicity and hydrophobicity of the microspheres (SPIO-Gn). The dynamic nature of the imine-containing dendronized microspheres (SPIO-Gn) can be "fixed" by locking the reversible 2,6-diiminopyridyl moieties with metal cations (Zn2+, Co2+, and Ni2+) to afford kinetically stable dendronized microspheres (SPIO-Gn-M). Isolation of these microspheres is facilitated by convenient magnetic separation by an externally applied magnetic field. Characterization of these novel organic-inorganic hybrid microspheres has been performed by various techniques using UV/visible absorption and Fourier transform infrared spectroscopies, transmission electron microscopy, thermogravimetric analysis, and a vibrating sample magnetometer. We have demonstrated the stability and reversible switching of hydrophilicity/hydrophobicity by contact-angle measurements. In particular, the hydrophilic SPIO-NH2 microspheres demonstrated a contact angle of 42 +/- 2 degrees when a drop of water was added to a SPIO-NH2-coated mica surface. On the other hand, the hydrophobic SPIO-Gn-M dendronized microspheres demonstrated a contact angle of 85 +/- 2 degrees , an observation that involves an increase of the contact angle of over 40 degrees . Furthermore, when a drop of water was placed on a dynamic SPIO-Gn-coated mica surface, the contact angle of the water droplet decreased in time. Comparatively, the rate of decrease of the contact angle is H2O > 1% Co(OAc)2/H2O > N,N'-dimethylformamide/H2O (1:1).