Multifunctional Hybrid Fe2O3-Au Nanoparticles for Efficient Plasmonic Heating
Published on: February 20, 2016
Magnetic properties of Fe(x)Pt(y)Au(100-x-y) nanoparticles
Vikas Nandwana1, Girija S Chaubey, Yunpeng Zhang
1Department of Physics, The University of Texas at Arlington, Arlington, Texas 76019, USA.
Abstract:
Fe(x)Pt(y)Au(100-x-y) nanoparticles of size 3.5 nm were prepared by polyol reduction of platinum acetylacetonate and gold acetate and the thermal decomposition of iron pentacarbonyl. The as-synthesized nanoparticles with disordered fcc structure were then heat treated to transform to the L1(0) structure with high magnetocrystalline anisotropy. By tuning the stoichiometry of the Fe(x)Pt(y)Au(100-x-y) nanoparticles, the phase transition temperature was reduced by more than 200 degrees C. After the annealing 500 degrees C, for instance, the highest coercivity of 18 kOe was obtained from the Fe51Pt36Au13 nanoparticles which is substantially higher compared to 2 kOe for Fe51Pt49 nanoparticles annealed at the same temperature. In addition to the high coercivity, the saturation magnetization value obtained from Fe51Pt36Au13 nanoparticles was 47 emu/g which is similar to that for the Fe51Pt49 nanoparticles, indicating that there is no trade-off between the coercivity and the saturation magnetization upon Au doping.
More Related Videos
09:06Visualizing Uniaxial-strain Manipulation of Antiferromagnetic Domains in Fe1+YTe Using a Spin-polarized Scanning Tunneling Microscope
Published on: March 24, 2019
11:49A Continuous-flow Photocatalytic Reactor for the Precisely Controlled Deposition of Metallic Nanoparticles
Published on: April 10, 2019
Related Concept Videos
01:31Ferromagnetism
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.