Marginal leakage of two newer glass-ionomer-based sealant materials assessed using micro-CT
1Key Laboratory for Oral Biomedical Engineering, School and Hospital of Stomatology, Wuhan University, Luoyu Road 237, 430079 Wuhan, Hubei, PR China.
Objectives:
To test newer glass-ionomer-based materials as sealant materials. One glass-ionomer sealant was light-cured to obtain an early setting reaction. The null-hypothesis tested was: there is no difference in marginal leakage of sealants produced with high-viscosity glass-ionomer, with and without energy supplied, and that of glass-carbomer, in comparison with resin composite sealants in vitro.
Methods:
Materials used were Clinpro, Ketac Molar Easymix and Glass-Carbomer. Sealants were placed in the occlusal surface of 89 molar teeth, thermocycled for 5000 cycles and evaluated using micro-CT for silver nitrate penetration depth at the enamel-sealant interface by two trained evaluators. Data were analysed, using ANOVA and Scheffe's test.
Results:
Glass-carbomer sealants showed one or more 'fracture lines' in the material and at the enamel-material interface, filled with a kind of transparent, but not black coloured, material. High-viscosity glass-ionomer sealants with and without energy supplied had statistically significantly lower mean marginal leakage scores than sealants produced by composite resin (p<0.01). No marginal leakage was found in the high-viscosity glass-ionomer group without energy supplied.
Conclusions:
The high-viscosity glass-ionomer (Ketac Molar Easymix) sealants had lower marginal leakage than resin composite sealants, and should be tested in vivo. Glass-carbomer sealants were non-interpretable.