Effect of film thickness and particle size on cracking stresses in drying latex films

Huai Nyin Yow1, Monika Goikoetxea, Lucas Goehring

  • 1Dept. of Chemical Engineering and Biotechnology, BP Institute, University of Cambridge, Madingley Road, Cambridge CB3 0EZ, UK.

Journal of Colloid and Interface Science
|September 21, 2010
PubMed

More Related Videos

Challenges in Rheological Characterization of Highly Concentrated Suspensions — A Case Study for Screen-printing Silver Pastes08:42

Challenges in Rheological Characterization of Highly Concentrated Suspensions — A Case Study for Screen-printing Silver Pastes

Published on: April 10, 2017

In situ Grazing Incidence Small Angle X-ray Scattering on Roll-To-Roll Coating of Organic Solar Cells with Laboratory X-ray Instrumentation06:49

In situ Grazing Incidence Small Angle X-ray Scattering on Roll-To-Roll Coating of Organic Solar Cells with Laboratory X-ray Instrumentation

Published on: March 2, 2021

Related Concept Videos

Factors Affecting Dissolution: Particle Size and Effective Surface Area01:23

Factors Affecting Dissolution: Particle Size and Effective Surface Area

Dissolution kinetics, an essential aspect of oral drug delivery, is significantly influenced by the drug's particle size. According to the Noyes-Whitney dissolution model, the dissolution rate correlates directly with the drug's surface area. The larger the surface area, the higher the drug's solubility in water, leading to a faster drug dissolution rate. Reducing particle size increases the effective surface area, enhancing the dissolution process. Micronization and nanosizing are employed to...
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...