Effect of applying a sustained force during bonding orthodontic brackets on the adhesive layer and on shear bond...

The objective of this research was to investigate the effect of applying a sustained seating force during bonding on the adhesive layer and on shear bond strength (SBS) of orthodontic brackets. Forty human premolars divided into two groups were included in the study. Stainless steel brackets were bonded to the premolars with Transbond XT light cure adhesive and Transbond Plus Self Etch Primer (SEP). The brackets in both groups were subjected to an initial seating force of 300 g for 3 seconds, sufficient to position the bracket. The seating force was maintained throughout the 40 seconds of light curing in group 2. SBS was tested 24 hours after bracket bonding with a shear blade using an Instron testing unit at a crosshead speed of 2 mm/minute. A Student's t-test was used to compare the bond strength of the two groups and a chi-square test to compare the frequencies of the adhesive remnant index (ARI) scores. The mean SBS was significantly different between the two groups (P=0.025). The bond strength was higher (mean 8.15±0.89 MPa) in group 2 compared with group 1 (mean 7.39±1.14 MPa). There was no significant difference (P=0.440) in the ARI scores between the two groups. Applying a sustained seating force during orthodontic bracket bonding improves bond strength but does not change the distribution of the ARI scores.