In Vivo Characteristics of Premixed Calcium Phosphate Cements When Implanted in Subcutaneous Tissues and Periodontal...

Previous studies showed that water-free, premixed calcium phosphate cements (Pre-CPCs) exhibited longer hardening times and lower strengths than conventional CPCs, but were stable in the package. The materials hardened only after being delivered to a wet environment and formed hydroxyapatite as the only product. Pre-CPCs also demonstrated good washout resistance and excellent biocompatibility when implanted in subcutaneous tissues in rats. The present study evaluated characteristics of Pre-CPCs when implanted in subcutaneous tissues (Study I) and used for repairing surgically created two-wall periodontal defects (Study II). Pre-CPC pastes were prepared by combining CPC powders that consisted of CPC-1: Ca(4)(PO(4))(2)O and CaHPO(4), CPC-2: α-Ca(3)(PO(4))(2) and CaCO(3) or CPC-3: DCPA and Ca(OH)(2) with a glycerol at powder-to-liquid mass ratios of 3.5, 2.5, and 2.5, respectively. In each cement mixture, the Ca to P molar ratio was 1.67. The glycerol contained Na(2)HPO(4) (30 mass %) and hydroxypropyl methylcellulose (0.55 %) to accelerate cement hardening and improve washout resistance, respectively. In Study I, the test materials were implanted subcutaneously in rats. Four weeks after the operation, the animals were sacrificed and histopathological observations were performed. The results showed that all of the implanted materials exhibited very slight or negligible inflammatory reactions in tissues contacted with the implants. In Study II, the mandibular premolar teeth of mature beagle dogs were extracted. One month later, two-wall periodontal bone defects were surgically created adjacent to the teeth of the mandibular bone. The defects were filled with the Pre-CPC pastes and the flaps replaced in the preoperative position. The dogs were sacrificed at 1, 3 and 6 months after surgery and sections of filled defects resected. Results showed that one month after surgery, the implanted Pre-CPC-1 paste was partially replaced by bone and was converted to bone at 6 months. The pockets filled with Pre-CPC-2 were completely covered by newly formed bone in 1 month. The Pre-CPC-2 was partially replaced by trabecular bone in 1 month and was completely replaced by bone in 6 months. Examination of 1 month and 3 month samples indicated that Pre-CPC-2 resorbed and was replaced by bone more rapidly than Pre-CPC 1. Both Pre-CPC pastes were highly osteoconductive. When implanted in periodontal defects, Pre-CPC-2 was replaced by bone more rapidly than Pre-CPC-1.