Preparation of poly(acrylic)/SiO2/EuL3 x 2H2O, hybrid thin films from monodispersed colloidal silica

In this study, poly(acrylic)/SiO2/EuL3 x 2H2O hybrid thin films were prepared from various acrylic monomers (MMA and EDMA/TMPTA), lanthanide metal complexes (EuL3 x 2H2O, L = pyridine carboxylic acid), and monodispersed colloidal silica with a coupling agent, 3-(trimethoxysilyl)propyl methacrylate (MSMA). It is a combination of the sol-gel reaction, thermal polymerization, and spin coating. The silica content in the hybrid thin films is fixed at 20 wt%, and the EuL3 x 2H2O content is varied from 0.01 g to 0.07 g. FTIR and EA analysis confirms the chemical structure of the prepared EuL3 x 2H2O and poly(acrylic)/SiO2/EuL3 x 2H2O hybrid thin films. UV-Vis spectra and n&k analysis shows that the hybrid thin film has good transparency in visible light. The refractive index of hybrid thin films can be effectively controlled through the EuL3 x 2H2O content. The PL spectra shows that the strongest emission peak occurs at 615 nm and the emission intensity increases to the peak maximum at an EuL3 x 2H2O content of 0.05 g. Both TGA and PL analysis show that the prepared hybrid thin films from the crosslinked acrylic polymer moiety have much better film uniformity, thermal stability, and fluorescence properties. The TEM diagram shows that the MSMA/SiO2/EuL3 x 2H2O particles with a size 15-20 nm are well dispersed in the reaction solution. The SEM diagram shows that the particle distribution in the prepared hybrid thin films is uniform and no phase separation is observed. Finally, AFM analysis indicates that the prepared hybrid thin films have an excellent surface planarity.