Immobilization of urease on nanostructured polymer membrane and preparation of urea amperometric biosensor

A new matrix for enzyme immobilization of urease was obtained by incorporating rhodium nanoparticles (5% on activated charcoal) and chemical bonding of chitosan with different concentration (0.15%; 0.3%; 0.5%; 1.0%; 1.5%) in previously chemically modified AN copolymer membrane. The basic characteristics of the chitosan modified membranes were investigated. The SEM analyses were shown essential morphology change in the different modified membranes. Both the amount of bound protein and relative activity of immobilized enzyme were measured. A higher activity (about 77.44%) was measured for urease bound to AN copolymer membrane coated with 1.0% chitosan and containing rhodium nanoparticles. The basic characteristics (pH(opt), T(opt), thermal, storage and operation stability) of immobilized enzyme on this optimized modified membrane were also determined. The prepared enzyme membrane was used for the construction of amperometric biosensor for urea detection. Its basic amperometric characteristics were investigated. A calibration plot was obtained for urea concentration ranging from 1.6 to 23 mM. A linear interval was detected along the calibration curve from 1.6 to 8.2mM. The sensitivity of the constructed biosensor was calculated to be 3.1927 μAmM(-1)cm(-2). The correlation coefficient for this concentration range was 0.998. The detection limit with regard to urea was calculated to be 0.5mM at a signal-to-noise ratio of 3. The biosensor was employed for 10 days while the maximum response to urea retained 86.8%.