Toughening of epoxy matrices with reduced single-walled carbon nanotubes

Reduced single-walled carbon nanotubes (r-SWCNT) are shown to react readily at room temperature under inert atmosphere conditions with epoxide moieties, such as those in triglycidyl p-amino phenol (TGAP), to produce a soft covalently bonded interface around the SWCNT. The soft interface is compatible with the SWCNT-free cross-linked cured matrix and acts as a toughener for the composite. Incorporation of 0.2 wt % r-SWCNT enhances the ultimate tensile strength, toughness and fracture toughness by 32, 118, and 40%, respectively, without change in modulus. A toughening rate (dK(IC)/dwt(f)) of 200 MPa m(0.5) is obtained. The toughening mechanism is elucidated through dynamic mechanical analyses, Raman spectroscopy and imaging, and stress-strain curve analyses. The method is scalable and applicable to epoxy resins and systems used commercially.