Novel low-molecular-weight hypromellose polymeric films for aqueous film coating applications

The concentration of hypromellose (HPMC) is known to significantly impact the viscosity of coating solutions. The purpose of this study was to determine the viscosity of novel low-molecular-weight (LMW) HPMC products as a function of polymer concentration. The mechanical properties and water vapor permeability of free films prepared from these novel LMW HPMC polymers were also determined and the results were compared with films prepared with conventional HPMC. Solutions of LMW and conventional HPMC 2910 and 2906 containing up to 40% polyethylene glycol (PEG) 400 were prepared and the viscosities were measured using a Brookfield viscometer. Solutions were then cast onto glass plates and stored at 30?C and 50% relative humidity until films were formed. A Chatillon digital force gauge attached to a motorized test stand was used to quantify the mechanical properties of the films, whereas water vapor permeabilities were determined according to the ASTM E96 M-05 water method. As expected, the novel LMW polymer solutions exhibited significantly lower viscosities than the conventional comparators at equivalent polymer concentrations. Film strength of the LMW materials was lower than films prepared from the conventional HPMC solutions, although this effect was not as evident for the HPMC 2906 chemistry. Increasing concentrations of the plasticizer resulted in decreased tensile strength and Young?s modulus and increased elongation as well as increased water vapor permeability, irrespective of polymer type. No statistical difference was found between the tensile strength to Young?s modulus ratios of the F chemistry LMW and conventional HPMC polymer films.