Scanning electrochemical microscopy studies of micropatterned copper sulfide (Cu(x)S) thin films fabricated by a wet...

Patterned copper sulfide (Cu(x)S) microstructures on Si (1 1 1) wafers were successfully fabricated by a relatively simple solution growth method using copper sulfate, ethylenediaminetetraacetate and sodium thiosulfate aqueous solutions as precursors. The Cu(x)S particles were selectively deposited on a patterned self-assembled monolayer of 3-aminopropyltriethoxysilane regions created by photolithography. To obtain high quality Cu(x)S films, preparative conditions such as concentration, proportion, pH and temperature of the precursor solutions were optimized. Various techniques such as optical microscopy, atomic force microscopy (AFM), X-ray diffraction, optical absorption and scanning electrochemical microscopy (SECM) were employed to examine the topography and properties of the micro-patterned Cu(x)S films. Optical microscopy and AFM results indicated that the Cu(x)S micro-pattern possessed high selectivity and clear edge resolution. From combined X-ray diffraction analysis and optical band gap calculations we conclude that Cu(9)S(5) (digenite) was the main phase within the resultant Cu(x)S film. Both SECM image and cyclic voltammograms confirmed that the Cu(x)S film had good electrical conductivity. Moreover, from SECM approach curve analysis, the apparent electron-transfer rate constant (k) in the micro-pattern of Cu(x)S dominated surface was estimated as 0.04 cm/s. The SECM current map showed high edge acuity of the micro-patterned Cu(x)S.