Shear bond strength of a hot pressed Au-Pd-Pt alloy-porcelain dental composite

The purpose of this study was to evaluate the effect of hot pressing on the shear bond strength of a Au-Pt-Pd alloy-porcelain composite.

Several metal-porcelain composites specimens were produced by two different routes: conventional porcelain fused to metal (PFM) and hot pressing. In the latter case, porcelain was hot pressed onto a polished surface (PPPS) as well as a roughened one (PPRS). Bond strength of all metal-porcelain composites were assessed by the means of a shear test performed in a universal test machine (crosshead speed: 0.5 mm/min) until fracture. Interfaces of fractured specimens as well as undestroyed interface specimens were examined with optical microscope, stereomicroscope, Scanning Electron Microscope (SEM) and Energy Dispersive X-Ray Spectroscopy (EDS). The data were analyzed using one-way ANOVA followed by Tuckey's test (p<0.05).

Shear bond strength of conventional PFM specimens were in line with the upper range of literature data (83±14 MPa). Hot pressing proved to significantly increase bond strength between metal and porcelain (p<0.05). For both polished and roughened surface the shear bond strength values for hot pressed specimens were 120±16 MPa and 129±5 MPa, respectively, which represents an improvement of more than 50% relatively to a conventional PFM. Roughened surface did not have a significant effect on bond strength of hot pressed specimens (p>0.05).

This study shows that it is possible to significantly improve metal-porcelain bond strength by applying an overpressure during porcelain firing.