Uptake of fluoride from aqueous solution on nano-sized hydroxyapatite: examination of a fluoridated surface layer

Hydroxyapatite (Ca(10)(PO(4))(6)(OH)(2), HAP), both as a synthetic material and as a constituent of bone char, can serve as an effective and relatively inexpensive filter material for fluoride (F(-)) removal from drinking water in low-income countries. Fluoride uptake on HAP can occur through different mechanisms, which are, in principle, influenced by solution composition. Suspensions of HAP (2 g L(-1)) were equilibrated under controlled pH conditions (pH 6.5, 7.3, 9.5) at 25 °C for 28 d after the addition of different F(-) concentrations (0.5-7.0 mM). The reacted HAP solids were examined with Transmission Electron Microscopy (TEM), Fourier Transform Infrared Spectroscopy (FTIR), X-ray Photoelectron Spectroscopy (XPS), and Nano Secondary Ion Mass Spectroscopy (NanoSIMS). Fluoride uptake on HAP was dependent on pH, with the highest capacity at pH 6.5; the lowest uptake was found at pH 9.5. Under all experimental conditions, the thermodynamically stable mineral phase was fluorapatite, (Ca(10)(PO(4))(6)F(2), FAP). Fluoride uptake capacity was quantified on the basis of FTIR and XPS analysis, which was consistent with F(-) uptake from solution. The results of XPS and NanoSIMS analyses indicate that a fluoridated surface layer with a thickness of several nanometers is formed on nanosized HAP.