Influence of abutment height and surface roughness on in vitro retention of three luting agents

This study evaluated the effects of abutment height, airborne-particle abrasion, and type of cement on the tensile resistance to dislodgement of cement-retained implant restorations.

Three groups of 12 standardized abutments each were prepared with different heights (4 mm, 5 mm, and 6 mm) using a milling machine. Crowns were cast in cobalt-chrome using the lost-wax technique, airborne particle-abraded using 50-Μm aluminum oxide, and cleaned with acetone. Restorations were cemented using a noneugenol acrylic urethane cement, a resin-modified glass ionomer, or a zinc oxide-noneugenol cement. A 5-kg load was applied for 10 minutes. Samples were kept at 37°C and 100% humidity overnight. A tensile force was applied to the crown using a testing machine at a crosshead speed of 5 mm/minute until failure occurred. Next, the abutments were airborne particle-abraded with 50-Μm aluminum oxide, and the cementation and testing procedures were repeated. The effects of cement, abutment height, and surface treatment were evaluated statistically.

There were significant differences among the cements. The resin-modified glass ionomer provided the greatest retention in all the tested conditions, while the zinc oxide-noneugenol cement produced the lowest retention values. Significant differences were also detected between 4-mm and 6-mm abutments, with the 6-mm abutments being more retentive. No differences were found between 4-mm and 5-mm abutments or between 5-mm and 6-mm abutments. The effect of airborne-particle abrasion was also found to be significant. A maximum increase of 90 N in retention force was observed after airborne-particle abrasion for the 5-mm abutments cemented with the acrylic urethane cement.

Cement, airborne-particle abrasion, and abutment height can significantly influence retention of implant-supported crowns. Different parameters, including those specific to the patient, should be considered in the selection of a luting agent.