Remineralization of enamel subsurface lesions with casein phosphopeptide-amorphous calcium phosphate: A quantitative
1Department of Conservative Dentistry and Endodontics, A. B. Shetty Memorial Institute of Dental Sciences, Deralakatte, Mangalore, Karnataka, India.
Aim:
The objective of this study was to quantitatively evaluate the remineralization potential of casein phosphopeptide-amor-phous calcium phosphate paste on enamel subsurface lesions using scanning electron microscopy with energy dispersive X-ray analysis (SEM-EDX).
Materials And Methods:
Ninety enamel specimens were prepared from extracted human molars. All specimens were evaluated for mineral content (% weight) using SEM-EDX. The specimens were placed in demineralizing solution for four days to produce artificial carious lesions. The mineral content (calcium/phosphorus ratios, Ca/P ratios) was remeasured using SEM-EDX. The specimens were then randomly assigned to five study groups and one control group of 15 specimens per group. Except for the control group, all group specimens were incubated in remineralizing paste (CPP-ACP paste) for 7, 14, 21, 28, and 35 days twice daily for three minutes. The control group received no treatment with remineralizing paste. All the 90 specimens were stored in artificial saliva at 37°C. After remineralization, the mineral content (% weight) of the samples was measured using SEM-EDX.
Results:
All the study groups showed very highly significant differences between Ca/P ratios of the demineralized and remineralized samples. There was no significant difference seen in the control group.
Conclusion:
CPP-ACP paste could significantly remineralize the artificial enamel subsurface lesions in vitro: the remineralizing rates increasing with the time for which the samples were kept in the remineralizing paste. Energy dispersive X-ray analysis is an efficient way to quantitatively assess the changes in mineral content during demineralization and in vitro remineralization processes.