Photocatalytic activity of low temperature oxidized Ti-6Al-4V

Numerous advanced surface modification techniques exist to improve bone integration and antibacterial properties of titanium based implants and prostheses. A simple and straightforward method of obtaining uniform and controlled TiO(2) coatings of devices with complex shapes is H(2)O(2)-oxidation and hot water aging. Based on the photoactivated bactericidal properties of TiO(2), this study was aimed at optimizing the treatment to achieve high photocatalytic activity. Ti-6Al-4V samples were H(2)O(2)-oxidized and hot water aged for up to 24 and 72 h, respectively. Degradation measurements of rhodamine B during UV-A illumination of samples showed a near linear relationship between photocatalytic activity and total treatment time, and a nanoporous coating was observed by scanning electron microscopy. Grazing incidence X-ray diffraction showed a gradual decrease in crystallinity of the surface layer, suggesting that the increase in surface area rather than anatase formation was responsible for the increase in photocatalytic activity.