Evaluation and comparison of castability between an indigenous and imported Ni-Cr alloy
Ganesh Ramesh1, T V Padmanabhan, Padma Ariga
1Department of Prosthodontics, Sree Balaji Dental College and Hospital, Chennai, India. rameshganesh@yahoo.com
Context:
Since 1907 casting restorations have been in use in dentistry. Numerous companies have been manufacturing and marketing base metal alloys. Gold was a major component of casting alloys. But alloys with less than 65% gold tarnished easily and the increase in cost of gold post-1970s lead to the revival of base metal alloys such as nickel-chromium and cobalt-chromium alloys which were in use since 1930s.
Aim:
This study was conducted to evaluate and compare the castability between an indigenous alloy and an imported alloy, as imported base metal alloys are considered to be expensive for fabrication of crowns and bridges.
Materials And Methods:
This study was conducted to evaluate and compare the castability (for the accurate fabrication of crowns and bridges) between an indigenous base metal alloy-Non-ferrous Materials Technology Development Centre (NFTDC), Hyderabad (Alloy A) -and an imported base metal alloys (Alloy B). Castability measurement was obtained by counting the number of completely formed line segments surrounding the 81 squares in the pattern and later calculating the percentage values. The percentage obtained was taken as the castability value for a particular base metal alloy. The percentage of castability was determined by counting only the number of completely cast segments in a perfect casting (81 × 2 = 162), and then multiplying the resulting fraction by 100 to give the percentage completeness.
Statistical Analysis Used:
The Student t-test was used.
Results:
When the castability of alloys A and B was compared, the calculated value was less than the tabular value (1.171 < 2.048) leading to the conclusion that castability between alloys A and B is insignificant. Therefore we conclude that both the alloys have the same castability.
Conclusions:
Using the above-mentioned materials and following the method to test castability, we were able to derive favorable results. As the results were satisfactory, we can conclude that the castability of the indigenous alloy is on par with the imported alloy.
Related Concept Videos
01:03Precipitation Gravimetry
In determining nickel by gravimetric analysis, a precipitant of ethanolic dimethylglyoxime is added to a hot nickel salt solution. This is quickly followed by the dropwise addition of dilute ammonia solution until precipitation occurs. A...
01:18Mechanical Characteristics of Steel
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used to...