A feasibility study for evaluation of mechanical properties of articular cartilage with a two-electrode electrical
Yusuke Morita1, Hideo Kondo, Naohide Tomita
1Department of Biomedical Engineering, Doshisha University, 1-3 Tatara Miyakodani, Kyotanabe, Kyoto, 610-0394, Japan. ymorita@mail.doshisha.ac.jp
Background:
Since articular cartilage has important mechanical properties such as load-bearing, shock absorption and lubrication for activities in daily life, it is important to evaluate the mechanical properties of repaired cartilage in terms of whether those properties are the same as those of natural cartilage. The purpose of this study was to investigate the effectiveness of an electrical impedance method for quantitatively measuring the mechanical properties of cartilage.
Methods:
Cartilage specimens were harvested from porcine knee joint, and two kinds of enzyme-treated cartilages were prepared to investigate the correlation between mechanical and electrical properties resulting from changes in the structure of the extracellular matrix. Collagenase solution and hyaluronidase solution were used to digest the collagen fibril and proteoglycan, respectively. Electrical impedance measurement, indentation test and biochemical analysis were carried out for the enzyme-treated cartilages.
Results:
The water content increased with enzyme treatment time, and the permeability of the treated cartilages increased with decreasing glycosaminoglycan content for both types of enzyme-treated cartilages. The aggregate modulus and the electrical resistivity for both types of enzyme-treated cartilages decreased with increasing permeability after 12-h treatment. The aggregate modulus and the electrical resistivity for both types of treated cartilages decreased with increasing water content and permeability after 24-h treatment. The electrical resistivity and the aggregate modulus of articular cartilage depended not only on the water content, but also on the permeability, and the electrical resistivity for both types of enzyme-treated cartilages was found to be significantly linearly correlated with the aggregate modulus.
Conclusions:
These results showed that the aggregate modulus of articular cartilage can be estimated by measuring its electrical impedance.